Part A (Epoxy): 20kg
Part B (Hardener): 10kg
Mix Ratio: Part A: Part B=2:1
Barrel A Size: 30*30*37cm
Barrel B Size: 25*25*29cm
HM-Q2Z is two components, high thixotropic paste structural adhesive, mainly used for repairing and leveling of bridge bearing pad stone
• Good thixotropic, easy to scrape;
• Good thixotropic, easy to scrape;
• Repairing and leveling of bridge bearing pad stone.
• Repairing and leveling of bridge bearing pad stone.
Product Characteristics
• Strength increasing quickly, which will reduce the padding setting time and greatly improve the construction efficiency and equipment turnover;
• -20℃～40℃ large curing temperature range, better for outdoor and cold area application;
• Good curing performance, high compressive strength and bonding strength, good toughness and impact resistance, good aging and medium resistance (acid, alkali and water etc.)
Product Characteristics
• Strength increasing quickly, which will reduce the padding setting time and greatly improve the construction efficiency and equipment turnover;
• -20℃～40℃ large curing temperature range, better for outdoor and cold area application;
• Good curing performance, high compressive strength and bonding strength, good toughness and impact resistance, good aging and medium resistance (acid, alkali and water etc.)
Application Range
• Making the surface flat but not smooth, letting the top surface elevation accuracy, making the pedestal bearing surface under fully behind the bearing pad on the stone and eliminate the phenomenon of local edge escapes.
• At the same time, by using our HM-Q2Z leveling adhesive, the two edges bearing pad stones under one beam or the top of the bearing pad stone on the abutment at the same elevation in horizontal, this will avoid bias, initial shear and uneven force.
Application Range
• Making the surface flat but not smooth, letting the top surface elevation accuracy, making the pedestal bearing surface under fully behind the bearing pad on the stone and eliminate the phenomenon of local edge escapes.
• At the same time, by using our HM-Q2Z leveling adhesive, the two edges bearing pad stones under one beam or the top of the bearing pad stone on the abutment at the same elevation in horizontal, this will avoid bias, initial shear and uneven force.
HM-20 Unidirectional Carbon Fiber Wrap
HM-1.2T Unidirectional Carbon Fiber Strip
HM-MJ50/100 Prestressed CFRP Plate System
| Technical Parameters | |
| HM-Q2Z BEARING PAD STONE LEVELING ADHESIVE | |
| Appearance | Part A: Viscous Paste |
| Part B: Viscous Paste | |
| Mixture Ratio | 2:1 |
| Operation time, 25℃ | ≥40min |
| Finger touch dry time, 25℃ | ≥2h |
| Compressive strength, MPa | ≥65 |
| Bending strength, MPa | ≥50 |