Part A (Epoxy): 20kg
Part B (Hardener): 1kg
Mix Ratio: Part A: Part B=20:1
Barrel A Size: 30*30*37cm
Barrel B Size: 8*8*10cm
HM-Q20D is two component ,high thixotropic paste structural adhesive, mainly used for repairing and leveling of bridge piers, abutment, the surface of the plate beam and chiseled position which will lay the jack after.
• Good thixotropic, easy to paste;
• Good thixotropic, easy to paste;
• Repairing and leveling of bridge piers, abutment, the surface of the plate beam and chiseled position which will lay the jack after;
• Repairing and leveling of bridge piers, abutment, the surface of the plate beam and chiseled position which will lay the jack after;
Characteristics of Adhesive
• Based on unsaturated resin, strength increasing fast, which can insure lying of jack lifting of bridge. Can be done synchronously. The strength can reach 80% of its highest strength within 30 min after curing;
• Good curing performance, high compressive strength and bonding strength, good toughness and impact resistance, good aging and medium resistance (acid, alkali and water etc.).
Characteristics of Adhesive
• Based on unsaturated resin, strength increasing fast, which can insure lying of jack lifting of bridge. Can be done synchronously. The strength can reach 80% of its highest strength within 30 min after curing;
• Good curing performance, high compressive strength and bonding strength, good toughness and impact resistance, good aging and medium resistance (acid, alkali and water etc.).
Application Range
• That can make jack and piers afford stress together while and lifting bridge, at the same time it can reduce the damage of Jack cylinder body and accidents which would caused by uneven or defects of the bridge pier platform and some equipment failure.
Application Range
• That can make jack and piers afford stress together while and lifting bridge, at the same time it can reduce the damage of Jack cylinder body and accidents which would caused by uneven or defects of the bridge pier platform and some equipment failure.
HM-20 Unidirectional Carbon Fiber Wrap
HM-1.2T Unidirectional Carbon Fiber Strip
HM-MJ50/100 Prestressed CFRP Plate System
| Technical Parameters | ||
| HM-Q20D bearing replacement repairing adhesive | ||
| Appearance | Part A: Viscous Paste | |
| Part B: Viscous Paste or Powder | ||
| Mixture Ratio | 20:1 | |
| Operation time, 25℃ | ≥15min | |
| Finger touch dry time, 25℃ | ≥40min | |
| Compressive strength, MPa | 2h | ≥30 |
| 4h | ≥32 | |
| 8h | ≥33 | |
| 12h | ≥35 | |
| Cohesive Pulling Strength, MPa (C30) | 2.5 | |